| Tipo di pagamento: | L/C,T/T,D/P,D/A,Paypal,Others |
| Incoterm: | FOB,CFR,CIF,EXW,FAS,FCA,CPT,CIP,DEQ,DDP,DDU,DAF,DES |
| Quantità di ordine minimo: | 5 Ton |
| Trasporti: | Ocean,Land,Air,Express |
| Porta: | Shanghai Port,Tianjin Port,Qingdao Port |
Materiale: 2B, Serie 600, Serie 300, Serie 500, Serie 200, Serie 400
Standard: JIS, AiSi, ASTM, GB, DIN, EN
Luogo D'origine: Cina
Specie: Bobina, Piatto
Certificazione: RoHS, ISO, IBR, BV, Sgs
Tolleranza: ± 1%
Servizio Di Elaborazione: Flessione, Saldatura, Decoiling, Punzonatura, Taglio
Technique: Cold Rolled Hot Rolled
Surface: BA/2B/NO.1/NO.3/NO.4/8K/HL/2D/1D
Material: 201,202,301,302,303,304,304L,304N1,309S,310S,316,316L,316Ti,316N,317,317L,321,409L,410,420,430,904,904L,etc
Sample: Provided
Spessore: 0.2~6mm
Width: 1000~2000mm
Standard: GB, JIS, ASTM, AISI
Grado: 200/300/400/500/600/700/800/900 series/duplex stainless steel
| Unità vendibili | : | Ton |
| Tipo pacchetto | : | Packaging standard del settore o secondo i requisiti del cliente |
The file is encrypted. Please fill in the following information to continue accessing it
La bobina in acciaio inossidabile di tipo 310S è un nichel di cromo ad alta temperatura in acciaio inossidabile austenitico con elevata resistenza allo scorrimento che resiste all'ossidazione a temperature fino a 2000 ° F nell'aria secca. Il tipo 310s costituisce una scala tenace ad alta temperatura ed è resistente allo spalling e si comporta meglio del tipo 309 nelle applicazioni di ciclismo termico. Il tipo 310 ha una buona resistenza al solfidazione e una buona resistenza alla carburizzazione in atmosfere moderatamente in carburi. Il tipo 310S è la versione a basso contenuto di carbonio di tipo 310 ed è utilizzata per facilitare la fabbricazione a causa della sua migliore formabilità e saldabilità. Il tipo 310S non è magnetico nelle condizioni di lavoro ricotto e a freddo ed è resistente alla corrosione come la bobina di tipo 304/304L.
| Element | 310S |
| Carbon | 0.08 |
| Chromium | 24.0-26.0 |
| Nickel | 19.0-22.0 |
| Manganese | 2.00 |
| Silicon | 1.50 |
| Phosphorus | 0.045 |
| Sulfur | 0.030 |
| Property | 310S |
| Yield Strength, min. (ksi) | 30 |
| Tensile Strength, min. (ksi) | 75 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 95 |
| Property | 310S |
| Density, lb/in3 | 0.290 |
| Modulus of Elasticity, psi | 29.0 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 8.8 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 8.0 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 30.7 |
Componente chimico in acciaio inossidabile
| Grade | C | Si | Mn | P | S | Ni | Cr | Mo |
| 201 | ≤0.15 | ≤0.75 | 5.5-7.5 | ≤0.06 | ≤0.03 | 3.5-5.5 | 16.0-18.0 | - |
| 202 | ≤0.15 | ≤1.0 | 7.5-10.0 | ≤0.06 | ≤0.03 | 4.-6.0 | 17.0-19.0 | - |
| 301 | ≤0.15 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 6.0-8.0 | 16.0-18.0 | - |
| 302 | ≤0.15 | ≤1.0 | ≤2.0 | ≤0.035 | ≤0.03 | 8.0-10.0 | 17.0-19.0 | - |
| 304 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 8.0-10.5 | 18.0-20.0 | |
| 304L | ≤0.03 | ≤1.0 | ≤2.0 | ≤0.035 | ≤0.03 | 9.0-13.0 | 18.0-20.0 | |
| 309S | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 12.0-15.0 | 22.0-24.0 | |
| 310S | ≤0.08 | ≤1.5 | ≤2.0 | ≤0.035 | ≤0.03 | 19.0-22.0 | 24.0-26.0 | |
| 316 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 |
| 316L | ≤0.03 | ≤1.0 | ≤2.0 | ≤0.045 | ≤0.03 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 |
| 321 | ≤0.08 | ≤1.0 | ≤2.0 | ≤0.035 | ≤0.03 | 9.0-13.0 | 17.0-19.0 | - |
| 410 | ≤0.15 | ≤1.0 | ≤1.0 | ≤0.035 | ≤0.03 | - | 11.5-13.5 | - |
| 430 | 0.12 | ≤0.75 | ≤1.0 | ≤0.040 | ≤0.03 | ≤0.60 | 16.0-18.0 | - |
| 904L | ≤2.0 | ≤0.045 | ≤1.0 | ≤0.035 | - | 23.0-28.0 | 19.0-23.0 | 4.0-5.0 |
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now